MALBEX WBI

COMPANY FOR THE PRODUCTION, REPRESENTATION AND SALES OF REFRACTORY MATERIALS

Product Catalog

FIRED PERICLASE AND PERICLASE-SPINEL BRICK PRODUCTS

Periclase brick products of standard quality and highly fired periclase brick products are made on the basis of natural magnesium oxide, with different contents of silicon and calcium oxide and low content of iron oxide, synthetically produced high-purity magnesium oxide and electrofused magnesium oxide with large crystals.

Periclase-spinel brick products are made from burnt natural magnesium oxide, with a low content of silicon, calcium and iron oxide, synthetically produced high-purity magnesium oxide, electrofused magnesium oxide, and burnt and electrofused spinel.

Burnt periclase and periclase-spinel brick products, due to their characteristics, are used for lining units in the cast iron and steel-making, cement, lime, glass and non-ferrous metal industries.

Burnt periclase and periclase-spinel bricks
Chemical analysis, % Physical properties
MgO CaO SiO2 Fe2O3 Al2O3 Residual carbon, % Volumetric weight, mm/cm3 Theoretical porosity Vol.% Compressive strength, N/mm2
BOMMAG-RK10EC8 97,5 <1,2 <0,7 <0,5 <0,1 > 8 3.00 - 3,06 < 5 > 45
BOMMAG-RK10EC12 97,5 <1,2 <0,7 <0,5 <0,1 > 12 2,98 - 3,04 < 6 > 40
BOMMAG-RK10EC14 97,5 <1,2 <0,7 <0,5 <0,1 > 14 2,94 - 3,00 < 6 > 38
BOMMAG-RK10EC16 97,5 <1,2 <0,7 <0,5 <0,1 > 16 2,92 - 2,98 < 7 > 35
BOMMAG-RK7EC10 97,2 <1,5 <0,7 <0,5 <0,1 > 6 2,96 - 3,02 < 5 > 42
BOMMAG-RK7EC12 97,2 <1,5 <0,7 <0,5 <0,1 > 6 2,95 - 3,01 < 5 > 40
BOMMAG-RK7EC14 97,2 <1,5 <0,7 <0,5 <0,1 > 6 2,94 - 3,00 < 6 > 38
BOMMAG-RK7EC16 97,2 <1,5 <0,7 <0,5 <0,1 > 6 2,92 - 2,98 < 6 > 35
BOMMAG-RK5EC6 97,0 <1,6 <0,8 <0,5 <0,1 > 6 3,00 - 3,06 < 6 > 50
BOMMAG-RK5EC8 97,0 <1,6 <0,8 <0,5 <0,1 > 8 2,98 - 3,04 < 5 > 45
BOMMAG-RK5EC12 97,0 <1,6 <0,8 <0,5 <0,1 > 12 2,95 - 3,01 < 6 > 40
BOMMAG-RK5EC14 97,0 <1,6 <0,8 <0,5 <0,1 > 14 2,92 - 2,98 < 6 > 38
BOMMAG-RK5EC16 97,0 <1,6 <0,8 <0,5 <0,1 > 16 2,90 - 2,96 < 7 > 35
BOMMAG-RK3EC8 96,8 <1,6 <0,9 <0,6 <0,1 > 8 2,98 - 3,04 < 5 > 45
BOMMAG-RK3EC12 96,8 <1,6 <0,9 <0,6 <0,1 > 12 2,95 - 3,01 < 5 > 40
BOMMAG-RK3EC14 96,8 <1,6 <0,9 <0,6 <0,1 > 14 2,94 - 3,00 < 6 > 38
BOMMAG-RK3EC16 96,8 <1,6 <0,9 <0,6 <0,1 > 16 2,92 - 2,98 < 7 > 35
BOMMAG-RKEC6 95,5 <2,2 <1,2 <0,9 <0,3 > 6 3,00 - 3,06 < 4 > 45
BOMMAG-RKEC8 96,0 <2,1 <1,1 <0,9 <0,3 > 8 2,98 - 3,04 < 5 > 45
BOMMAG-RKEC10 96,0 <2,0 <1,0 <0,6 <0,1 > 10 2,95 - 3,02 < 5 > 45
BOMMAG-RKEC12 96,5 <1,9 <1,0 <0,6 <0,1 > 12 2,95 - 3,01 < 6 > 40
BOMMAG-RKEC14 96,5 <1,7 <1,0 <0,7 <0,1 > 14 2,92 - 2,98 < 6 > 40
BOMMAG-RKC6 96,5 <1,8 <1,0 <0,6 <0,1 > 6 3,00 - 3,06 < 5 > 50
BOMMAG-RKC8 96,5 <1,8 <1,0 <0,6 <0,1 > 8 2,98 - 3,04 < 5 > 45
BOMMAG-RKC10 96,5 <1,8 <1,0 <0,6 <0,1 > 10 2,95 - 3,01 < 6 > 42
BOMMAG-RKC12 96,5 <1,8 <1,0 <0,6 <0,1 > 12 2,92 - 2,98 < 6 > 40

RESIN BOUND ALUMINOPERICLASE CARBON BRICK PRODUCTS

Resin bonded aluminopericlase-carbon brick products include a wide range of products with different contents of burnt bauxite, burnt and electrofused corundum, burnt natural magnesium oxide, synthetically produced high-purity magnesium oxide, electrofused magnesium oxide with large crystals, burnt and electrofused spinel, with the addition of various parts of high-quality natural graphite, resin as a binder and various additives and antioxidants.

The selection of the most optimal ratios of individual components and pressing with high individual pressures make it possible to obtain high-quality bricks with the most optimal characteristics in individual conditions of their use.

Resin bound aluminopericlase carbon brick products
Chemical analysis, % Physical properties
MgO CaO SiO2 Fe2O3 Al2O3 Residual carbon, % Volumetric weight, mm/cm3 Theoretical porosity Vol.% Compressive strength, N/mm2
BOMMAGAL-RB90C8 10,0 <0,7 <4,0 <1,5 76-78 > 6 2,95 - 3,05 4-5 > 45
BOMMAGAL-RB90C10 12,0 <0,4 <2,7 <1,0 78-80 > 8 3,00 - 3,10 6 > 45
BOMMAGAL-RB80C8 80,0 <1,7 <1,0 <0,7 16,6 > 8 3,00 - 3,10 6 > 60
BOMMAGAL-RB80C10 80,0 <1,7 <1,0 <0,7 16,6 > 10 3,00 - 3,05 6 > 55
BOMMAGAL-RB70C8 24,0 <0,5 <2,7 <1,1 65-66 > 6 2,95 - 3,05 4-5 > 45
BOMMAGAL-RB70C10 67,0 <1,5 <1,2 <0,8 23-24 > 6 2,95 - 3,05 2-5 > 45
BOMMAGAL-RB8C8 7,0 <0,2 <3,0 <0,7 80,0 > 8 3,09 - 3,15 8 > 80
BOMMAGAL-RB8C10 7,0 <0,2 <3,0 <0,7 80,0 > 10 3,06 - 3,12 8 > 75
BOMMAGAL-RB7C6 7,0 <0,2 <6,4 <1,20 75-77 > 6 2,85 - 2,95 4-5 > 45
BOMMAGAL-RB7C8 7,0 <0,2 <3,0 <0,7 80,0 > 8 3,09 - 3,15 8 > 80

FIREPROOF MORTERS

They are used for laying burnt periclase and periclase-spinel bricks, burnt magnesite-chromite and chromomagnesite bricks in the lining of thermal units. The production program presents many qualities of refractory mortars, produced with different grain sizes.

Fireproof morters
Chemical analysis, % Physical properties
MgO CaO SiO2 Fe2O3 Al2O3 Cr2O3 Granule size, mm Expiry date, months.
BOMMAG-MB7V 90 < 2,8 < 4,5 < 1,7 < 0,5 - 0 - 0,2 6
BOMMAG-MB2V 92 < 1,4 < 2,5 < 1,6 < 0,3 - 0 - 0,2 6
BOMMAG-MHB3V 81 < 2,0 < 3,5 < 12,0 < 0,3 - 0 - 0,5 6
BOMMAG-MB7 88 < 3,0 < 6,5 < 4,0 < 0,5 - 0 - 0,5 6

MAGNESITE RAMMING MASSES

Magnesite ramming masses from the BOMMAGRAM series are made from calcined natural magnesium oxide with various contents of silicon and calcium oxide, and low content of iron oxide, synthetically produced high-purity magnesium oxide, and electrofused magnesium oxide and concentrate with various types of binders and additives.

The masses are used for new linings in units in ferrous and non-ferrous metallurgy, as well as for repairing linings during operation.

*C - Chemistry, OC - Organic chemistry

Magnesite ramming masses
Chemical analysis, % Physical properties
MgO min CaO max SiO2 max Fe2O3 max Al2O3 Granule size, mm Required quantity, kg/dm3 Maximum application temperature ℃ Connection
BOMMAGPATCH-21 GK 93,0 1,6 2,2 1,5 0,5 0-2 2,7 1800 CC
BOMMAGPATCH-31 GM 93,5 2,2 1,8 1,0 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-32 GM 93,0 2,2 2,2 1,0 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-33 GM 92,5 2,7 2,5 1,0 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-34 GM 92,0 3,0 2,8 1,0 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-35 GM 91,0 3,0 3,6 1,0 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-36 GM 90,0 3,0 4,0 1,0 0,5 0-3 2,7 1700 CC
BOMMAGRAM-61 85,0 3,0 6,5 - - 0-6 2,7 1700 C
BOMMAGRAM-41BV 93,0 2,0 3,0 1,6 0,3 0-4 2,7 1700 C
BOMMAGRAM-33GM 94,5 2,1 1,4 0,5 0,15 0-3 2,7 1750 C
BOMMAGRAM-P 63C 94,5 2,4 1,7 0,9 0,5 0-3 2,8 1700 OC
BOMMAGRAM-65 BM 78,0 8,0 12 4,0 3,0 0-6 2,7 >1600 C
BOMMAGRAM-80 C 70,0 15,0 1,5 6,0 0,5 0-3 2,0 >1750 C
BOMMAGRAM-80 H 65,0 7,0 6,0 5,0 0,5 0-3 2,6 >1750 OC

MAGNESITE MASSES FOR SHOTCRETING

Magnesite masses for shotcreting from the BOMMAGPATCH GTM/GTS/GTF series are made from calcined natural magnesium oxide with various contents of silicon and calcium oxide, low content of iron oxide, synthetically obtained high-purity magnesium oxide and electrofused magnesium oxide, with different types of binders and additives.

These masses are characterized by high adhesive properties, good sintering tendency, and also very good resistance to the erosive and corrosive effects of molten metal.

Magnesite masses for gunning are used for cold and hot repairs in ferrous and non-ferrous metallurgy.

Magnesite masses for shotcreting
Chemical analysis, % Physical properties
MgO min CaO SiO2 Fe2O3 Al2O3 Granule size, mm Required quantity, kg/dm3 Maximum application temperature ℃ Connection
BOMMAGPATCH-30 GTS 92,0 2,0 3,9 1,0 0,5 0-3 2,7 1750 CC
BOMMAGPATCH-30 GTM 94,0 2,2 1,5 1,0 0,5 0-3 2,7 1750 CC
BOMMAGPATCH-30 GTM 94,0 2,2 1,5 1,0 0,5 0-3 2,7 1750 CC
BOMMAGPATCH-30 GTF (+P2O5 =1,4%) 91,0 2,2 1,5 1,0 0,5 0-3 2,7 1750 CC
BOMMAGPATCH-31 GTS 89,5 1,9 5,3 1,5 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-31 GTM 90,0 1,7 4,0 1,5 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-31 GTF (+P2O5=1,6%) 89,5 1,7 4,0 1,5 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-31 GTR 90,5 1,7 4,0 1,5 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-32 GTS 89,5 1,9 5,5 1,5 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-32 GTM 91,0 1,9 4,2 1,5 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-33 GTS 89,5 1,9 6,0 1,5 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-33 GTM 90,0 1,9 4,5 1,5 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-34 GTS 88,0 2,5 7,0 1,5 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-34 GTM 89,5 2,5 5,0 1,5 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-35 GTS 87,0 2,5 7,0 1,5 0,5 0-3 2,7 1700 CC
BOMMAGPATCH-35 GTM 89,0 2,5 5,5 1,5 0,5 0-3 2,7 1730 CC
BOMMAGPATCH QHR 302 76,0 6,0 11,0 1,5 3,0 0-3 2,5 1750 CC

BUFFER MAGNESITE BACKFILLING MASSES

BOMMAGFILL-40 is a dry magnesite buffer mass for backfilling and filling intermediate layers of industrial unit linings.

BOMMAGFILL-270H and BOMMAGFILL-20H are specially designed dry masses for backfilling of slide gate valves in the steel industry.

Magnesite masses for shotcreting
Chemical analysis, % Physical properties
MgO min CaO max SiO2 max Fe2O3 max Al2O3 max Granule size, mm Required quantity, kg/dm3 Maximum application temperature ℃ Connection
BOMMAGFILL-40 85,0 3,0 6,5 - - 0-4 2,2 1650 -
BOMMAGFILL-40 v (+P2O5=1,2%) 85,0 3,0 4,5 0,6 1,0 0-4 2,2 1650 CC
BOMMAGFILL-0,1 v (+P2O5=1,2%) 92,0 2,2 1,4 0,6 0,3 0-0,1 2,0 1650 CC
BOMMAGFILL-40 v (+P2O5=1,5%) 0,5 0,5 16 1,6 80,0 0-4 2,1 1650 CC
BOMMAGFILL-60 v (+P2O5=1,5%) 0,4 0,5 16 1,6 82,0 0-6 2,2 1650 CC
BOMMAGFILL-EBT 57,0 0,4 33 8,0 0,6 0-6 2,5 1720 -

MAGNESITE MASSES FOR SHOTCRETING THE LINING OF INTERMEDIATE LADLES

Magnesite masses for gunning the lining of intermediate ladles in the steel industry are made on the basis of calcined natural magnesium oxide and olivine, with the addition of special types of binders and additives, which ensure the use of masses for large series of steel casting during its continuous casting.

Mixtures for shotcreting intermediate ladles
Chemical analysis, % Physical properties
MgO min CaO max SiO2 max Fe2O3 max Al2O3 max Granule size, mm Required quantity, kg/dm3 Maximum application temperature ℃ Connection
BOMMAGGUN-10 TZ 91,0 2,0 3,6 1,5 0,5 0-1 1,4 1720 CC
BOMMAGGUN-01 T 88,0 1,7 5,8 0,3 1,5 0-0,1 1,4 1720 CC
BOMMAGGUN-10 T 88,4 1,8 6,4 0,3 0,2 0-0,5 1,4 1720 CC
BOMMAGGUN-10 F 68,0 1,6 24,0 2,5 1,2 0-0,5 1,3 1710 CC
↑